Additional Data on the Effect of Cooling Rate on the Fatigue Properties of Carburized Steels

In the previous post, the effects of a cooling rate change after carburizing, due to a change in steel bar diameter, on core fatigue properties was examined.  The data was developed for a Ni-Cr-Mo low alloy steel (SAE 4320), and … Continue reading

Posted in News | Tagged , , , , , , , | 2 Comments

Effect of Cooling Rate after Carburizing on the Fatigue Properties of Carburized Steels

In earlier posts, the fatigue properties of various carburized low alloy steels were examined.  Both case and core properties were evaluated.  Since carburized components are manufactured in various section sizes, it can be expected that cooling rates in the cores … Continue reading

Posted in News | Tagged , , , , , , , , , | Leave a comment

Comparison of Case Hardening by Carburizing Versus Surface Induction Hardening

In past postings, the case and core properties of case hardened steels have been discussed.  These discussions have included the fatigue properties of both carburized and surface induction hardened steels. Carburizing is usually employed on carbon or low alloy steels … Continue reading

Posted in News | Tagged , , , , , , , | 2 Comments

Comparison of Through-Induction Hardening with Conventional Hardening

Two methods are often used to through harden and low alloy steels.  The well recognized conventional hardening method involves heating to an appropriate austenitizing temperature for a specific length of time in a furnace with or without a protective atmosphere. This … Continue reading

Posted in News | Tagged , , , , , , , | 6 Comments