Fatigue Properties of Modified Steels Carburized at High Temperatures

The objective of phase XI is to compare the performance of carburized steel in bending and axial fatigue loading conditions. Carburization is a surface heat treatment process which adds carbon to the surface of a material to increase its hardness … Continue reading

Posted in News | Tagged , , , , , , , , , , | Leave a comment

Strength and Fatigue Life versus Carbon Content at High Hardness (60 HRC)

The strength, fatigue and hardness data for several iterations with a high hardness level, around 60 HRC are shown in Table 1. The steels in these iterations are both plain carbon and low alloy grades with carbon contents ranging from … Continue reading